35CrMo is the specification number of alloy structural steel (alloy quenched and tempered steel), which is mainly used to manufacture important parts in various machines bearing impact, bending and torsion and high load. The unified digital code of 35CrMo alloy structural steel (alloy quenched and tempered steel) is a30352, and the executive standard is GB / t3077-2015

35crmo

35CrMo (2 sheets)

Italy: 35crmo4

NBN: 34crmo4

Sweden: 2234

Daily standard: scm432 / sccrm3

It is used to manufacture important parts in various machines bearing impact, bending and torsion and high load, such as herringbone gear, crankshaft, hammer rod, connecting rod and fasteners of steel rolling mill, main shaft and axle of steam turbine engine, engine transmission parts, large motor shaft, perforator in petroleum machinery, boiler bolts with working temperature lower than 400 ℃, nuts with working temperature lower than 510 ℃, High pressure seamless thick wall conduit (temperature 450 ~ 500 ℃, no corrosive medium) in chemical machinery; It can also replace 40crni for manufacturing high load transmission shaft, steam turbine engine rotor, large section gear, support shaft (diameter less than 500mm), etc; Process equipment materials, pipes, welding materials, etc.

Used as important structural parts working under high load, such as transmission parts of vehicles and engines; Rotor, main shaft, heavy load transmission shaft and large section parts of steam turbine generator.

Carbon C: 0.32 ~ 0.40

Silicon Si: 0.17 ~ 0.37

Mn: 0.40 ~ 0.70

Sulfur s: allowable residual content ≤ 0.035

Phosphorus P: allowable residual content ≤ 0.035

Cr: 0.80 ~ 1.10

Nickel: allowable residual content ≤ 0.30

Copper Cu: allowable residual content ≤ 0.30

Mo: 0.15 ~ 0.25

Tensile strength σ b (MPa): ≥985(100)

Yield strength σ s (MPa): ≥835(85)

Elongation δ 5 (%): ≥12

Reduction of area ψ (%):  ≥45

Impact energy Akv (J): ≥ 63

Impact toughness value α kv (J/cm²):  ≥78(8)

Hardness: ≤ 229hb

Sample size: sample blank size is 25mm

Heat treatment specification and metallographic structure

Heat treatment specification: quenching 850 ℃, oil cooling; Tempering 550 ℃, water cooling, oil cooling.

Steel grade: 35CrMo

Sample blank size / mm: 25

Heat treatment | quenching | heating temperature / ℃ | first quenching: 850

Heat treatment | quenching | heating temperature / ℃ | second quenching: –

Heat treatment | quenching | coolant: Oil

Heat treatment | tempering | heating temperature / ℃: 550

Heat treatment | tempering | coolant: water, oil

Mechanical properties | tensile strength σ b/MPa|≥: 980

Mechanical properties | yield point σ s/MPa|≥: 835

Mechanical properties | elongation δ 5(%)|≥: 12

Mechanical properties | surface shrinkage ψ(%)| ≥: 45

Mechanical properties | impact absorption energy Akv / J | ≥: 63

Delivery state hardness HBS | ≥: 229

Delivery status: delivery in heat treatment (normalizing, annealing or high temperature tempering) or non heat treatment status, and the delivery status shall be indicated in the contract.